冷轧高磁感取向硅钢板型缺陷研究

Study on Plate Defects of Cold Rolled High Magnetic Induction Oriented Silicon Steel

探讨了武钢硅钢事业DMS森吉米尔轧机轧制高磁感取向硅钢(Hi-B)时出现的板形缺陷瓢曲的形成机理,通过现场的试验和分析,实际轧制过程中减少ASU频繁动作、合理配置辊系、合理设定板型曲线有利于抑制瓢曲的产生。

To investigate the cause of the silicon appear DMS rolling mills rolling high magnetic induction oriented silicon steel(Hi-B) when the plate-shaped defect formation mechanism of buckling through testing and analysis site, the actual process of reducing rolling ASU frequent moves, the rational allocation of rolls, a reasonable set of plate buckling curves help to curb production.