针对现有金属增材制造设备昂贵、成形效率低等问题,提出金属熔融涂覆增材制造(MFCAM).以锡铅合金为原料,开展基础工艺实验,研究流量、成形速度和层厚对多层单道成形件表面形貌特征的影响规律.通过统计分析影响因素,提高成形件表面质量,采用显微图像观察,结合波纹度对多层单道试件层间结合状态进行评估.研究结果表明,金属熔融涂覆增材制造成形效率为50mm^3/s,成形件表面波纹度的轮廓算术平均偏差为0.944 8,证明了MFCAM新工艺的可行性及高效性.
A novel method of metal fused-coating additive manufacturing(MFCAM)was proposed aiming at the high cost and low forming efficiency of the existing metal additive manufacturing equipment.Sn63-Pb37 alloy was used in this basic experiment,and the influences of flow rate,deposition speed and layer thickness on the surface morphology characteristics of multi-layer single pass specimen were analyzed.The surface quality of formed parts was improved through the analysis on these process parameters.The bonding state between layers of multi-layer single pass specimen was evaluated combined with waviness by using microscopic image observation.The forming efficiency can reach 50 mm3/s,and the arithmetical mean deviation of the cross-section profile is 0.944 8.The feasibility and efficiency of the MFCAM technology were verified.
作者
杜军
王鑫
任传奇
白浩
DU Jun;WANG Xin;REN Chuan-qi;BAI Hao(State Key Laboratory of Manufacturing System Engineering,Xi’an Jiaotong University,Xi'an710049,China)
出处
《浙江大学学报(工学版)》
EI
CAS
CSCD
北大核心
2018年第1期24-28,共5页
Journal of Zhejiang University:Engineering Science
基金
国家重点研发计划专项资助项目(2016YFB1100400)
装备预研教育部联合基金资助项目(6141A02022109)
中央高校基本科研业务费专项资金资助项目(xjj2016124)
关键词
增材制造
金属熔融涂覆
多层单道
表面形貌
锡63铅37
层厚
additive manufacturing
metal fused-coating
multilayer single-pass
surface appearance
Sn63-Pb37
layer thickness