摘要
The properties of lithium ferrites are very sensitive to chemical composition, synthesis method, and sintering techniques. Li–Ni–Co ferrites with compositional formula Li_(0.45-0.5x)Ni_(0.1)Co_xFe_(2.45-0.5x)O_4, where 0.00 ≤ x ≤ 0.1 in steps of 0.02 were prepared by chemical sol–gel method and sintered by microwave sintering technique. The x-ray diffraction patterns confirmed the formation of single phase with spinel structure in all the samples. The structural parameter viz.lattice constant, crystallite size, and x-ray density for these samples were studied and compared with those measured from samples of similar composition prepared by the sol–gel method and sintered by conventional sintering technique. Enhancement in the magnetic properties like Curie temperature, hysteresis parameters was observed by employing sol–gel synthesis combined with microwave sintering. The results obtained and mechanisms involved are discussed in the paper.
The properties of lithium ferrites are very sensitive to chemical composition, synthesis method, and sintering techniques. Li–Ni–Co ferrites with compositional formula Li_(0.45-0.5x)Ni_(0.1)Co_xFe_(2.45-0.5x)O_4, where 0.00 ≤ x ≤ 0.1 in steps of 0.02 were prepared by chemical sol–gel method and sintered by microwave sintering technique. The x-ray diffraction patterns confirmed the formation of single phase with spinel structure in all the samples. The structural parameter viz.lattice constant, crystallite size, and x-ray density for these samples were studied and compared with those measured from samples of similar composition prepared by the sol–gel method and sintered by conventional sintering technique. Enhancement in the magnetic properties like Curie temperature, hysteresis parameters was observed by employing sol–gel synthesis combined with microwave sintering. The results obtained and mechanisms involved are discussed in the paper.