摘要
Single-grain models with different cerium contents or structural parameters have been introduced to investigate the reversal magnetization behaviors in cerium-containing magnets. All the micromagnetic simulations are carried out via the object oriented micromagnetic framework(OOMMF). As for single(Nd,Ce)_2 Fe_(14)B type grain, the coercivity decreases monotonously with the increase of the cerium content. Four types of grain structure have been compared: single(Nd,Ce)_2 Fe_(14)B type, core((Nd,Ce)_2 Fe_(14)B)-shell(Nd_2 Fe_(14)B) type with 2 nm thick shell, core(Ce_2 Fe_(14)B)-shell(Nd_2 Fe_(14)B) type, and core(Nd_2 Fe_(14)B)-shell(Ce_2 Fe_(14)B) type. It is found that core((Nd,Ce)_2 Fe_(14)B)-shell(Nd_2 Fe_(14)B)type grain with 2 nm thick shell always presents the largest coercivity under the same total cerium content. Furthermore,the relationship between the coercivity and the shell thickness t in core((Nd,Ce)_2 Fe_(14)B)-shell(Nd_2 Fe_(14)B) type grain has been studied. When the total cerium content is kept at 20.51 at.%, the analyzed results show that as t varies from 1 nm to 7 nm, the coercivity gradually ascends at the beginning, then quickly descends after reaching the maximum value when t = 5 nm. From the perspective of the positions of nucleation points, the reasons why t affects the coercivity are discussed in detail.
Single-grain models with different cerium contents or structural parameters have been introduced to investigate the reversal magnetization behaviors in cerium-containing magnets. All the micromagnetic simulations are carried out via the object oriented micromagnetic framework(OOMMF). As for single(Nd,Ce)_2 Fe_(14)B type grain, the coercivity decreases monotonously with the increase of the cerium content. Four types of grain structure have been compared: single(Nd,Ce)_2 Fe_(14)B type, core((Nd,Ce)_2 Fe_(14)B)-shell(Nd_2 Fe_(14)B) type with 2 nm thick shell, core(Ce_2 Fe_(14)B)-shell(Nd_2 Fe_(14)B) type, and core(Nd_2 Fe_(14)B)-shell(Ce_2 Fe_(14)B) type. It is found that core((Nd,Ce)_2 Fe_(14)B)-shell(Nd_2 Fe_(14)B)type grain with 2 nm thick shell always presents the largest coercivity under the same total cerium content. Furthermore,the relationship between the coercivity and the shell thickness t in core((Nd,Ce)_2 Fe_(14)B)-shell(Nd_2 Fe_(14)B) type grain has been studied. When the total cerium content is kept at 20.51 at.%, the analyzed results show that as t varies from 1 nm to 7 nm, the coercivity gradually ascends at the beginning, then quickly descends after reaching the maximum value when t = 5 nm. From the perspective of the positions of nucleation points, the reasons why t affects the coercivity are discussed in detail.
作者
李磊
董生智
陈红升
姜瑞姣
李栋
韩瑞
周栋
朱明刚
李卫
孙威
Lei Li;Shengzhi Dong;Hongsheng Chen;Ruijiao Jiang;Dong Li;Rui Han;Dong Zhou;Minggang Zhu;Wei Li;Wei Sun
基金
supported by the National Natural Science Foundation of China(Grant Nos.51590882 and 51871063)