铁泥溶剂热法制备磁性材料及其在水溶液中对亚甲基蓝的吸附性 被引量:5

Synthesis of magnetic materials by solvothermal method with iron-mud and adsorption of methylene blue in aqueous solution
下载PDF
导出
摘要 以地下水厂含铁污泥为原料,利用一步溶剂热法制备出含有Fe3O4的磁性材料。采用磁学性质测量系统、X射线衍射仪、穆斯堡尔谱仪、X射线光电子能谱仪和扫描电镜对铁泥和磁性材料进行表征。结果表明:地下水厂铁泥含铁量较低(16.6%,质量分数),其杂质主要是硅和铝矿物,粒径约为70 nm,在磁场下不会迁移;经过溶剂热法处理后,生成含有Fe3O4的椭球形磁性材料,粒径达到1.5μm,比饱和磁化强度(Ms)可达18.9 A·m2/kg,在磁场下可迅速向磁极迁移并聚集,体现了良好的磁响应特征。磁性材料对水中亚甲基蓝的吸附效果接近粉末活性炭,在5 min内对10 mg/L亚甲基蓝的吸附效率达到92.3%。本研究方法可以处理含铁量较低的铁泥,实现铁泥的资源化利用,制备的磁性材料在染料废水处理中具有潜在的应用价值。 Magnetic material with ferroferric oxide was synthesized by one-step solvothermal method using iron mud with low-iron-content as the raw material. The obtained magnetic material was characterized by magnetic property measurement system (MPMS), X-ray diffraction (XRD), M?ssbauer spectroscopy, X-ray photoelectron spectroscopy (XPS) and scanning electron microscopy (SEM). The results show that the iron content in iron mud is only 16.6%(mass fraction), while the main impurities are silicon and aluminum oxides, iron mud with the average size of 70 nm does not have any magnetism. After solvothermal process, the obtained magnetic material contains ferroferric oxide and assumes a near-sphere shape with the average size of 1.5 μm. The material possesses well magnetic response, and the specific saturated magnetizing strength reaches 18.9 A?m2/kg, which can be easily magnetic separated from water. Dramatically, the adsorptivity of the material is nearly equivalent to powder active carbon, for example, the removal efficiency of methylene blue (10 mg/L) reaches to 92.3% in 5 min, which contributes to the chemical adsorption between the methylene blue and the material. Therefore, this facile solvothermal method can be applied to dispose iron mud with low-iron-content and make the mud into recoverable resource. Moreover, the prepared magnetic material has a potential application on the treatment of dye wastewater.
出处 《中国有色金属学报》 EI CAS CSCD 北大核心 2015年第4期1109-1115,共7页 The Chinese Journal of Nonferrous Metals
基金 国家自然科学基金资助项目(51238001 51108069 51378098) 吉林省自然科学基金资助项目(20130101038JC 20140520151JH)
关键词 四氧化三铁 亚甲基蓝 地下水厂 铁泥 溶剂热法 Fe3O4 methylene blue groundwater treatment plant iron mud solvothermal synthesis
  • 相关文献

参考文献12

二级参考文献118

共引文献188

同被引文献81

  • 1王颖,吕斯丹,李辛,吴英杰.去除水体中砷的研究进展与展望[J].环境科学与技术,2010,33(9):102-107. 被引量:28
  • 2宋云飞,周攀登,周健,肖柏喜,刘宵,李烨.白腐真菌生物法处理染料亚甲基蓝的研究[J].生物技术世界,2013,10(1):13-14. 被引量:4
  • 3Shchukin D, Sukhorukov G, Price R, et al. Halloysite nanotubes as biomimetic nanoreactors[J]. Small, 2005, 1(5): 510–513.
  • 4Vergaro V, Scarlino F, Bellomo C, et al. Drug-loaded p–olyelectrolyte microcapsules for sustained targeting of cancer cells[J]. Adv Drug Delivery Rev, 2011, 63(9): 847864.
  • 5Xie Y, Zhang Y, Ouyang J, et al. Mesoporous material Al-MCM-41 from natural halloysite[J]. Phys Chem Miner, 2014, 41(7): 497–503.
  • 6Jin J, Zhang Y, Ouyang J, et al. Halloysite nanotubes as hydrogen storage materials[J]. Phys Chem Miner, 2013, 41(5): 1–9.
  • 7Jin J, Fu L, Yang H, et al. Carbon hybridized halloysite nanotubes for high-performance hydrogen storage capacities[J]. Sci Rep, 2015, 5,12429.
  • 8Zhao Y, Abdullayev E, Vasiliev A, et al. Halloysite nanotubule clay for efficient water purification[J]. J Colloid Interface Sci, 2013, 406(18): 121–129.
  • 9He X, Yang Q, Fu L, et al. Synthesis and magnetic property of SiO2 coated Fe3O4/palygorskite[J]. Funct Mater Lett, 2015, 8(5): 1550056.
  • 10Hussain I, Singh N, Singh A, et al. Green synthesis of nanoparticles and its potential application[J]. Biotechnol Lett, 2015, 38(4): 1–16.

引证文献5

二级引证文献33

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部