The semisolid slurry of Al-Zn-Mg-Cu alloy was prepared through a self-designed water-cooled copper serpentine pouring channel(WSPC) machine. Influences of pouring temperature, the number of turns and the cooling water flow rate on the microstructure of the semisolid Al-Zn-Mg-Cu alloy slurry were investigated. The results show that the semisolid Al-Zn-Mg-Cu alloy slurry with satisfactory quality can be generated by the WSPC when the pouring temperature is in the range between 680 ℃ and 700 ℃. At a given pouring temperature, the average grain size of primary α-Al decreases and the shape factor increases with the increase of the number of turns. When the cooling water flow rate is 450 L·h^(-1), the obtained semisolid slurry is optimal. During the preparation of the semisolid Al-Zn-Mg-Cu alloy slurry with low superheat pouring, the alloy melt has mixed inhibition and convection flow characteristics by "self-stirring". When the alloy melt flows through the serpentine channel, the chilling effect of the inner wall of the channel, the convection and mixed inhibition of the alloy melt greatly promote the heterogeneous nucleation and grain segregation. This effect destroys the dendrite growth mode under traditional solidification conditions, and the primary nuclei gradually evolve into spherical or nearspherical grains.
The semisolid slurry of Al-Zn-Mg-Cu alloy was prepared through a self-designed water-cooled copper serpentine pouring channel(WSPC) machine. Influences of pouring temperature, the number of turns and the cooling water flow rate on the microstructure of the semisolid Al-Zn-Mg-Cu alloy slurry were investigated. The results show that the semisolid Al-Zn-Mg-Cu alloy slurry with satisfactory quality can be generated by the WSPC when the pouring temperature is in the range between 680 ℃ and 700 ℃. At a given pouring temperature, the average grain size of primary α-Al decreases and the shape factor increases with the increase of the number of turns. When the cooling water flow rate is 450 L·h^(-1), the obtained semisolid slurry is optimal. During the preparation of the semisolid Al-Zn-Mg-Cu alloy slurry with low superheat pouring, the alloy melt has mixed inhibition and convection flow characteristics by "self-stirring". When the alloy melt flows through the serpentine channel, the chilling effect of the inner wall of the channel, the convection and mixed inhibition of the alloy melt greatly promote the heterogeneous nucleation and grain segregation. This effect destroys the dendrite growth mode under traditional solidification conditions, and the primary nuclei gradually evolve into spherical or nearspherical grains.
基金
financially supported by the National Natural Science Foundation of China(Grant No.51701078)
China Postdoctoral Science Foundation(Grant Nos.2018M632846 and 2018T110756)
the Scientific Research Program of Hubei Provincial Education Department(Grant No.B2016053)