Effects of interlayer composition on bonding strength and interfacial microstructure of green joined CePO_4-ZrO_2 ceramics were studied. Green bodies of 25%CePO_4/ZrO_2 and ZrO_2 ceramics were joined by using interlayer composed of CePO_4 and ZrO_2 at 1450 ℃ for 120 min without applied pressure.The effects of CePO_4/(CePO_4+ZrO_2) ratio on the bond strength of the joints were investigated. Under the experimental conditions, the grain size of the particles grown in the joint is smaller than those in joined ceramics. The microstructure of the joint is more homogeneous than that of the matrix and without obvious cracks, pores and other defects.
Effects of interlayer composition on bonding strength and interfacial microstructure of green joined CePO_4-ZrO_2 ceramics were studied. Green bodies of 25%CePO_4/ZrO_2 and ZrO_2 ceramics were joined by using interlayer composed of CePO_4 and ZrO_2 at 1450 ℃ for 120 min without applied pressure.The effects of CePO_4/(CePO_4+ZrO_2) ratio on the bond strength of the joints were investigated. Under the experimental conditions, the grain size of the particles grown in the joint is smaller than those in joined ceramics. The microstructure of the joint is more homogeneous than that of the matrix and without obvious cracks, pores and other defects.
基金
ProjectsupportedbytheMinistryofEducationofChina (9914 3 )