摘要
采用加入木质素磺酸钠的方法改性脲醛树脂胶粘剂,以降低胶粘剂中游离甲醛为主要目的,主要研究了磺化木质素加入量对胶粘剂游离甲醛含量及拉伸强度的影响。实验结果表明磺化木质素加入量为30%时,胶粘剂的拉伸强度最大,达到8.67Mpa;磺化木质素的加入量为40%时,游离甲醛含量最小,为0.18%.
The UF resin adhesive was modified by lignosulfonate; the main idea was to deduce the free-formaldehyde in adhesive. The effect of LS on properties of product on free-formaldehyde and tensile strength was investigated. The experiment showed that tensile strength reached 8.67 Mpa when the product LS property 30% and free-formaldehyde decreased to 0.18% when the product LS property was 40%.