Two kinds of Nd 1+ x Ba 2- x Cu 3O 7- δ , the sintered samples and zone melted samples, were treated in pure Ar at 950 ℃. The substitution of Nd ions for Ba ions in the Nd 1+ x Ba 2- x Cu 3O 7- δ before and after the heat treatment was investigated by XRD. In order to know the effects of heat treatment, the T c and J c of samples with and without the heat treatment in Ar were comparatively studied. The results show that the substitution of Nd for Ba decreases, whereas T c and J c increase after the treatment. The Nd 1+ x Ba 2- x Cu 3O 7- δ samples were oxygenated in pure oxygen at 300 ℃ . Based on the XRD spectra it was found that the samples with x <0.4 can transform from tetragonal phase into orthorhombic phase after the oxygenation, whereas in the sample with x >0.4 no phase transition occurs even after a long time oxygenation.
Two kinds of Nd 1+ x Ba 2- x Cu 3O 7- δ , the sintered samples and zone melted samples, were treated in pure Ar at 950 ℃. The substitution of Nd ions for Ba ions in the Nd 1+ x Ba 2- x Cu 3O 7- δ before and after the heat treatment was investigated by XRD. In order to know the effects of heat treatment, the T c and J c of samples with and without the heat treatment in Ar were comparatively studied. The results show that the substitution of Nd for Ba decreases, whereas T c and J c increase after the treatment. The Nd 1+ x Ba 2- x Cu 3O 7- δ samples were oxygenated in pure oxygen at 300 ℃ . Based on the XRD spectra it was found that the samples with x <0.4 can transform from tetragonal phase into orthorhombic phase after the oxygenation, whereas in the sample with x >0.4 no phase transition occurs even after a long time oxygenation.
基金
ProjectsupportedbyNationalCenterforResearchandDevelopmentonSuperconductivity (863 CD0 2 0 10 5 )