ZrO 2-Al 2O 3 composite oxides and supported Ni catalysts were prepared, and characterized by N 2 adsorption /desorption, X-ray diffraction(XRD) an d X-ray photoelectron spectroscopy(XPS) techniques. The catalytic performance and carbon deposition was also investigated. This mesoporous composite oxide is shown to be a promising catalyst support. An increase in the catalytic activity and stability of methane and carbon dioxide reforming reaction was resulted from the zirconia addition, especially at 5wt% ZrO 2 content. The Ni catalyst supported ZrO 2-Al 2O 3 has a strong resistance to sintering and the carbon deposition in a relatively long-term reaction.
ZrO 2-Al 2O 3 composite oxides and supported Ni catalysts were prepared, and characterized by N 2 adsorption /desorption, X-ray diffraction(XRD) an d X-ray photoelectron spectroscopy(XPS) techniques. The catalytic performance and carbon deposition was also investigated. This mesoporous composite oxide is shown to be a promising catalyst support. An increase in the catalytic activity and stability of methane and carbon dioxide reforming reaction was resulted from the zirconia addition, especially at 5wt% ZrO 2 content. The Ni catalyst supported ZrO 2-Al 2O 3 has a strong resistance to sintering and the carbon deposition in a relatively long-term reaction.
基金
TheNationalNaturalScienceFoundationofChina(No.50 78094)
andChina 863High TechProgram (No .2 0 0 1AA32 4 0 50 )