摘要
The all-lithium salts of heteropoly acid Li_xXM_ 12O_ 40(HPA-Li)(X=P, Si; M=Mo, W) were obtained via ion exchange and characterized by means of IR and UV spectroscopies, TG and elemental analyses. The conductivity of the electrolytic solution consisting of Li_3PW_ 12O_ 40 and PC/DME mixing solvent(1/2.5, volume ratio) is up to 7.2×10 -2 S/cm, being higher than that of LiClO_4 as the electrolyte. The all-lithium salts were used as electrolytes in secondary lithium-ion batteries. The discharge capacity of the PAS/Li batteries with Li_3PW_ 12O_ 40 electrolyte solutions reaches to 148 (mA·h)/g and the cyclic life is up to 380 times, much better than those of commercialized products with LiClO_4 and LiAsF_6 as electrolytes.
The all-lithium salts of heteropoly acid Li_xXM_ 12O_ 40(HPA-Li)(X=P, Si; M=Mo, W) were obtained via ion exchange and characterized by means of IR and UV spectroscopies, TG and elemental analyses. The conductivity of the electrolytic solution consisting of Li_3PW_ 12O_ 40 and PC/DME mixing solvent(1/2.5, volume ratio) is up to 7.2×10 -2 S/cm, being higher than that of LiClO_4 as the electrolyte. The all-lithium salts were used as electrolytes in secondary lithium-ion batteries. The discharge capacity of the PAS/Li batteries with Li_3PW_ 12O_ 40 electrolyte solutions reaches to 148 (mA·h)/g and the cyclic life is up to 380 times, much better than those of commercialized products with LiClO_4 and LiAsF_6 as electrolytes.
基金
SupportedbytheNational 9.5KeyProgramFund(No .97 6 4 2 16 )andtheNationalNaturalScienceFoundationofChina(No.39970 84 2 )