The fragility of Al Ni Ce alloy melts with three kinds of different compositions, Al85Ni10Ce5, Al85Ni8Ce7, Al85Ni5Ce10(mole fraction, %), was studied using oscillating vessel viscometer and differential scanning calorimetry. Their fragility parameters obtained from experiments and theoretic calculation are: 238, 228 and 335 respectively. The results indicate that these three kinds of Al Ni Ce alloy melts are very fragile liquids, which kinetically show strong non Arrhenius behaviour in the Angell plot, so they have poor glass forming ability (GFA). The alloy melt Al85Ni5Ce10 has the largest fragility parameter among the three alloy melts. In the preparation of rapidly quenched amorphous ribbons, Al85Ni10Ce5 and Al85Ni8Ce7 can gain amorphous ribbons when the rotate speed of the roller reaches 800 r/min, while for Al85Ni5Ce10 it must exceed 1 000 r/min.
The fragility of Al Ni Ce alloy melts with three kinds of different compositions, Al85Ni10Ce5, Al85Ni8Ce7, Al85Ni5Ce10(mole fraction, %), was studied using oscillating vessel viscometer and differential scanning calorimetry. Their fragility parameters obtained from experiments and theoretic calculation are: 238, 228 and 335 respectively. The results indicate that these three kinds of Al Ni Ce alloy melts are very fragile liquids, which kinetically show strong non Arrhenius behaviour in the Angell plot, so they have poor glass forming ability (GFA). The alloy melt Al85Ni5Ce10 has the largest fragility parameter among the three alloy melts. In the preparation of rapidly quenched amorphous ribbons, Al85Ni10Ce5 and Al85Ni8Ce7 can gain amorphous ribbons when the rotate speed of the roller reaches 800 r/min, while for Al85Ni5Ce10 it must exceed 1 000 r/min.
出处
《中国有色金属学会会刊：英文版》
CSCD
2004年第1期78-81,共4页
Transactions of Nonferrous Metals Society of China
基金
Project ( 5 0 2 3 10 40 )supportedbytheNationalNaturalScienceFoundationofChina