Thin PVA/nickel acetate composite fibres were prepared by using sol-gel processing and electrospinning technique. After calcination of the above precursor fibres, NiO nanofibres with a diameter of 50-150 nm could be successfully obtained. The fibres were characterized by SEM, FT-IR, WAXD, respectively.
Thin PVA/nickel acetate composite fibres were prepared by using sol-gel processing and electrospinning technique. After calcination of the above precursor fibres, NiO nanofibres with a diameter of 50-150 nm could be successfully obtained. The fibres were characterized by SEM, FT-IR, WAXD, respectively.