新型PBT增韧剂对PBT增韧的研究

Study of Toughening of New Toughening Agengt on PBT

采用新型双官能化增韧剂SWR 6B对PBT及增强PBT进行增韧研究。结果表明 ,随着增韧剂SWR 6B用量的增加 ,PBT的冲击强度显著提高 ;当其质量分数为 10 %时 ,冲击强度为 10 0kJ/m2 ,是纯PBT的 2倍 ;在增强PBT中的效果也优于其它增韧剂 ;且SWR 6B在改善冲击强度的同时 ,材料的拉伸性能 ,弯曲性能下降较少 ,是一种比较理想的PBT增韧剂。同时对比了SWR 6B和美国杜邦MN PTW及法国阿托AX890 0等对PBT及增强PBT性能的影响。

The effects of a new dual-functional toughening agent SWR-6B on the toughening of PBT and reinforced PBT were studied. The results indicated that the impact strength enhanced obviously with the increase of the content of SWR-6B,and when the mass fraction of SWR-6B was up to 10%,the impact strength was 10.0kJ/m 2,which was about 2 times of that of pure PBT;the toughing effect of SWR-6B on reinforced PBT was better than those of other toughing agents. When the impact strength of PBT was improved by the addition of SWR-6B,the tensile and flexural properties decreased only a little, which showed SWR-6B was an ideal toughing agent for PBT. Comparisons of the toughing effects of SWR-6B with those of MN-PTW(Dupont,US) and AX8900(Atochem,France)on PBT were made.