K2AgIn3Se6 was synthesized by a molten-salt (alkali-metal polyselenide flux) reaction at 500 ℃. The orange red granular crystal crystallizes in monoclinic space group C2/c with cell parameters, a=1.16411(7) nm, b=1.16348(8) nm, c=2.14179(12) nm, V=2.8740(9) nm3, and Z=8. The crystal has a new two-dimensional structure containing 2∞[AgIn3Se6]2- anionic layers separated by K+ cations and the 2∞[AgIn3Se6]2- layer is constructed with corner-shared [AgSe4] and [InSe4] tetrahedra. The optical band gap of K2AgIn3Se6 was determined to be ca. 2.9 eV by UV/vis/NIR diffuse reflectance spectra.
K2AgIn3Se6 was synthesized by a molten-salt (alkali-metal polyselenide flux) reaction at 500 ℃. The orange red granular crystal crystallizes in monoclinic space group C2/c with cell parameters, a=1.16411(7) nm, b=1.16348(8) nm, c=2.14179(12) nm, V=2.8740(9) nm3, and Z=8. The crystal has a new two-dimensional structure containing 2∞[AgIn3Se6]2- anionic layers separated by K+ cations and the 2∞[AgIn3Se6]2- layer is constructed with corner-shared [AgSe4] and [InSe4] tetrahedra. The optical band gap of K2AgIn3Se6 was determined to be ca. 2.9 eV by UV/vis/NIR diffuse reflectance spectra.
基金
Project supported by the State Key Laboratory of Structural Chemistry for Unstable and Stable Species
China.