摘要
The complex coating on the MgO CaO clinker was prepared by dipping method and adding the second mineral to restrain the formation and expansion of the cracks. Meanwhile, the microstructure and the morphology of the coating and hydration resistance of the MgO CaO clinker were also investigated. The result shows that the coating consists mainly of Ca 2P 2O 7, MgO and CaCO 3, its thickness ranges from 5μm to 20μm, and the coating is dense and even, no micro cracks are observed. Also, the coating adheres closely to the matrix. The hydration resistance of the MgO CaO clinker after treatment is improved greatly, and the castables prepared with the treated MgO CaO clinker have better physical properties than MgO castable.
The complex coating on the MgO CaO clinker was prepared by dipping method and adding the second mineral to restrain the formation and expansion of the cracks. Meanwhile, the microstructure and the morphology of the coating and hydration resistance of the MgO CaO clinker were also investigated. The result shows that the coating consists mainly of Ca 2P 2O 7, MgO and CaCO 3, its thickness ranges from 5μm to 20μm, and the coating is dense and even, no micro cracks are observed. Also, the coating adheres closely to the matrix. The hydration resistance of the MgO CaO clinker after treatment is improved greatly, and the castables prepared with the treated MgO CaO clinker have better physical properties than MgO castable.