摘要
The Fe(OH) 3 precursor was prepared by solid-state reaction with Fe(NO 3 ) 3 ·9H 2 O,NaOH and dispersed poly-ethylene glycol at low heating temperature(25℃).Synthesis of iron oxide(γ-Fe 2 O 3 )nanoparticle was achieved by thermal decomposition of Fe(OH) 3 ·xH 2 O precursor.The nanoparticle was characterized by TG-DTA,X-ray diffra-ction,TEM etc.The results showed that the nanoparticle was composed ofγ-Fe 2 O 3 and was a better absorber for electromagnetic wave within the low frequency band.
The Fe(OH) 3 precursor was prepared by solid-state reaction with Fe(NO 3 ) 3 ·9H 2 O,NaOH and dispersed poly-ethylene glycol at low heating temperature(25℃).Synthesis of iron oxide(γ-Fe 2 O 3 )nanoparticle was achieved by thermal decomposition of Fe(OH) 3 ·xH 2 O precursor.The nanoparticle was characterized by TG-DTA,X-ray diffra-ction,TEM etc.The results showed that the nanoparticle was composed ofγ-Fe 2 O 3 and was a better absorber for electromagnetic wave within the low frequency band.
出处
《无机化学学报》
SCIE
CAS
CSCD
北大核心
2004年第4期479-482,共4页
Chinese Journal of Inorganic Chemistry
基金
国家自然科学基金资助项目(No.20271042)。