摘要
The microemulsion copolymerizations of acrylic acid (AA),acrylamide (AM),N-methylol acrylamide (NMA),methylmethacrylate (MMA),butyl acrylate (BA) and acrylonitrile (AN) initiated by the redox initiator ammonium persulfate (APS) and N,N,N′,N′-tetramethylethylenediamine (TMEDA) at ambient temperature were investigated.With this process high solids-content (44.0 wt%) and small (less than 50 nm) particle diameter copolymer latexes were attained.The effects of surfactants,the mechanical stabilities and application properties as an environmentally friendly self-crosslinking pigment printing binder with multifunctional groups were studied.
The microemulsion copolymerizations of acrylic acid (AA),acrylamide (AM),N-methylol acrylamide (NMA),methylmethacrylate (MMA),butyl acrylate (BA) and acrylonitrile (AN) initiated by the redox initiator ammonium persulfate (APS) and N,N,N′,N′-tetramethylethylenediamine (TMEDA) at ambient temperature were investigated.With this process high solids-content (44.0 wt%) and small (less than 50 nm) particle diameter copolymer latexes were attained.The effects of surfactants,the mechanical stabilities and application properties as an environmentally friendly self-crosslinking pigment printing binder with multifunctional groups were studied.
基金
FundedbytheNationalNaturalScienceFoundationofChi na(No.2 0 2 730 82 )