Thin PVA/cobalt acetate composite fibers were prepared by using sol-gel processing and electrospinning technique. After calcination of the above precursor fibers, Co3O4 nanofibers with a diameter of 50-150 nm could be successfully obtained. The fibers were characterized by SEM, FT-IR, WAXD, respectively.
Thin PVA/cobalt acetate composite fibers were prepared by using sol-gel processing and electrospinning technique. After calcination of the above precursor fibers, Co3O4 nanofibers with a diameter of 50-150 nm could be successfully obtained. The fibers were characterized by SEM, FT-IR, WAXD, respectively.