摘要
In this work, the effect of solid soluble temperature, cold treating temperature and ag-ing temperature on the mechanical properties of 0Cr12Mn5Ni4Mo3Al had been inves-tigated systemically. The results show that under the optimal parameters (solid solubletreatment 1050℃×40min, cold treatment -78℃×4h, aging treatment 520℃×2h) theproperties (strength and tenacity) could be up to its maximum.
In this work, the effect of solid soluble temperature, cold treating temperature and ag-ing temperature on the mechanical properties of 0Cr12Mn5Ni4Mo3Al had been inves-tigated systemically. The results show that under the optimal parameters (solid solubletreatment 1050℃×40min, cold treatment -78℃×4h, aging treatment 520℃×2h) theproperties (strength and tenacity) could be up to its maximum.