摘要
Influence of NH_4 Cl on the initial atmospheric corrosion of zinc was investigated viaquartz crystal microbalance (QCM) in laboratory at 80%RH and 25℃. The resultsshow that NH_4 Cl can accelerate the initial corrosion of zinc. Mass gain increase withthe exposure time, but mass gain in the later doesn't change obviously due to theformation of the insoluble simonkolleite on zinc surface in the presence of NH_4 Cl.Fourier transform infrared spectroscopy (FTIR) and X-ray diffraction (XRD) wasused to characterize the corrosion products. Zn_5Cl_2(OH)_8·H_2O,(NH_4)_2ZnCl_4 andZnO are the corrosion products on zinc. Brief discussion on the mechanisms of at-mospheric corrosion of zinc in the presence of NH_4 Cl was introduced.
Influence of NH_4 Cl on the initial atmospheric corrosion of zinc was investigated viaquartz crystal microbalance (QCM) in laboratory at 80%RH and 25℃. The resultsshow that NH_4 Cl can accelerate the initial corrosion of zinc. Mass gain increase withthe exposure time, but mass gain in the later doesn't change obviously due to theformation of the insoluble simonkolleite on zinc surface in the presence of NH_4 Cl.Fourier transform infrared spectroscopy (FTIR) and X-ray diffraction (XRD) wasused to characterize the corrosion products. Zn_5Cl_2(OH)_8·H_2O,(NH_4)_2ZnCl_4 andZnO are the corrosion products on zinc. Brief discussion on the mechanisms of at-mospheric corrosion of zinc in the presence of NH_4 Cl was introduced.