Fe-58at%Al alloy is undercooled up to 222 K (0.15TL) with the drop tube technique. It is found that there exists a critical undercooling about 185 K, beyond which a 揹endrite-equiaxed?growth morphology transition occurs in FeAl intermetallic compound. This transition is character-ized by sharp decrease of its grain size. Once the undercool-ing exceeds 215 K, the peritectic transformation is sup-pressed completely and a fibrous structure is formed, which results from the cooperative growth of FeAl and FeAl2 com-pounds.
Fe-58at%Al alloy is undercooled up to 222 K (0.15TL) with the drop tube technique. It is found that there exists a critical undercooling about 185 K, beyond which a 揹endrite-equiaxed?growth morphology transition occurs in FeAl intermetallic compound. This transition is character-ized by sharp decrease of its grain size. Once the undercool-ing exceeds 215 K, the peritectic transformation is sup-pressed completely and a fibrous structure is formed, which results from the cooperative growth of FeAl and FeAl2 com-pounds.
关键词
快速凝固
铝化铁
金属间合成
超低温条件
树突生长
rapid solidification, peritectic, dendrite growth, under-cooling, grain refining.