摘要
The calcium-containing active material of secondary alkaline zinc electrodes was prepared by a chemical coprecipitation method and characterized by scanning electron microscopy(SEM) and X-ray diffractometry(XRD). Their electrochemical performance was tested by the Galvanstatic charge-discharge method. The experimental results show that the sample synthesized at pH=11.15 has a typical calcium zincate crystal. The zinc electrode using this sample as active material shows higher discharge capacity, more negative discharge plateau potential and longer cycle lifetime.
The calcium-containing active material of secondary alkaline zinc electrodes was prepared by a chemical coprecipitation method and characterized by scanning electron microscopy(SEM) and X-ray diffractometry(XRD). Their electrochemical performance was tested by the Galvanstatic charge-discharge method. The experimental results show that the sample synthesized at pH=11.15 has a typical calcium zincate crystal. The zinc electrode using this sample as active material shows higher discharge capacity, more negative discharge plateau potential and longer cycle lifetime.
出处
《中国有色金属学会会刊：英文版》
CSCD
2004年第2期406-411,共6页
Transactions of Nonferrous Metals Society of China
基金
Project (5 970 10 0 8)supportedbytheNationalNaturalScienceFoundationofChina