在剂量为1×10^(17)cm^(-2)和温度为310℃下,观察到强束流脉冲钨离子注入H13钢所形成的空洞。探讨了空洞的形成原因并发现空洞能提高H13钢的硬度而使其磨损性能变差。
Under low dose temperature, voids formed by W-implanted H13 steel have been observed. Causes of voids formed are discussed. The hardness of H13 steel increases and wear resistance becomes bad.