The reverse transformation behavior of TiNi alloy wires prestrained at different temperatures is studied in this paper. Experimental results show that prestrain at different temperatures obviously affects the reverse transformation behavior of the TiNi alloy wire. A single peak appears on the DSC curves of wires prestrained at 253-313K (in the martensite state). However deformed at 333K, three consecutive peaks appear on the DSC curves of wires with a smaller prestrain and a single peak appears on the DSC curves of the wires with a larger prestrain. The recovery strain ratio of the wires prestrained at 253-313K are very similar. However, the ratio of the wire predeformed at 333K is obviously smaller than that of the wire prestrained in the martensite state.
The reverse transformation behavior of TiNi alloy wires prestrained at different temperatures is studied in this paper. Experimental results show that prestrain at different temperatures obviously affects the reverse transformation behavior of the TiNi alloy wire. A single peak appears on the DSC curves of wires prestrained at 253-313K (in the martensite state). However deformed at 333K, three consecutive peaks appear on the DSC curves of wires with a smaller prestrain and a single peak appears on the DSC curves of the wires with a larger prestrain. The recovery strain ratio of the wires prestrained at 253-313K are very similar. However, the ratio of the wire predeformed at 333K is obviously smaller than that of the wire prestrained in the martensite state.
基金
This work is funded by the National Natural Science Foundation
the Peoples Republic of China (No. 50071037)