Native corn starch and hydroxypropyl starch (HPS) based plastic films were prepared using the short pulp fiber as reinforcement and the glycerol as the plasticizer. The results of tensile test showed that the tensile strength and the elongation at break increased with the pulp contents. With the glycerol contents, the elongation at break increased considerably, but the tensile strength decreased. The water uptake of the films decreased with the pulp contents and hydroxypropylation, but increased with the glycerol contents. So it is concluded that the films was reinforced by pulp fiber and hydroxypropylation.
Native corn starch and hydroxypropyl starch (HPS) based plastic films were prepared using the short pulp fiber as reinforcement and the glycerol as the plasticizer. The results of tensile test showed that the tensile strength and the elongation at break increased with the pulp contents. With the glycerol contents, the elongation at break increased considerably, but the tensile strength decreased. The water uptake of the films decreased with the pulp contents and hydroxypropylation, but increased with the glycerol contents. So it is concluded that the films was reinforced by pulp fiber and hydroxypropylation.
出处
《天津科技大学学报》
CAS
2004年第A02期13-17,共5页
Journal of Tianjin University of Science & Technology