采用液态铸渗工艺生产出WC+Cr20金属基硬面复合材料。复合界面剪切强度483MPa,已接近母材强度。界面致密,呈冶金结合。
Using liquid osmose, to produce WC+Cr20 metallic matrix composites, an interfacial shear strength of 483MPa was measured which is close to the shear strength of matrix.Interface combination appeared metallurgically.