摘要
在强碱性电镀液中获取的非晶态Fe-Mo合金镀层表面存在大量微裂纹,往镀液中加入ZrO_2、TiO_2等微粒可以改善镀层的表面状态,从而使非晶态镀层的硬度、耐蚀性得到提高。
The amorphous of Fe-Mo alloy deposit with miniature cract has been obtained in a strong alkaline solution. The results showed that the hardness and the corrosion resistance increased with the addition of ZrO_2 and TiO_2 particles in the electrolyte.
出处
《材料保护》
CAS
CSCD
北大核心
1993年第11期15-17,共3页
Materials Protection