摘要
A nanostructured thermal barrier coating is prepared by air plasma spraying using the 8wt% Y_2O_3 partially stabilized zirconia nano-powder with an average grain size of 40 nm. The microstructure and phase composition of feedstock nano-powder and coating are investigated using SEM, TEM and XRD. It is found that the as-sprayed zirconia coating has an average grain size of 67 nm and mainly consistes of metastable tetragonal phase, together with some monoclinic phase and tetragonal phase. Thermal treatment results show that the grains of the nanostructured coating grow slightly below 900℃, whereas over 1000℃ the gains grow rapidly and monoclinic phase noticeably appeares.
A nanostructured thermal barrier coating is prepared by air plasma spraying using the 8wt% Y_2O_3 partially stabilized zirconia nano-powder with an average grain size of 40 nm. The microstructure and phase composition of feedstock nano-powder and coating are investigated using SEM, TEM and XRD. It is found that the as-sprayed zirconia coating has an average grain size of 67 nm and mainly consistes of metastable tetragonal phase, together with some monoclinic phase and tetragonal phase. Thermal treatment results show that the grains of the nanostructured coating grow slightly below 900℃, whereas over 1000℃ the gains grow rapidly and monoclinic phase noticeably appeares.
基金
NationalNaturalScienceFoundationofChina( 5 0 1760 0 5 )