聚醚醚酮与钴铬合金作为可摘局部义齿卡环材料的疲劳性研究

Study on the Fatigue Properties of Polyether Ether Ketone and Cobalt Chromium Alloy as Removable Partial Denture Clasp Materials

目的:比较聚醚醚酮、钴铬合金卡环在不同倒凹深度下的疲劳寿命,为临床卡环材料的选择提供依据。方法:聚醚醚酮和钴铬合金将制作的铸造卡环相应地进入基牙两种倒凹深度(0.25 mm和0.50 mm),进行位移控制疲劳弯曲实验得出初始载荷及循环次数。结果:对两种材料制作的卡环循环疲劳测试的统计学分析结果显示,位移为0.25 mm时,钴铬合金的初始载荷高于聚醚醚酮(P 0.05)。结论:聚醚醚酮的抗疲劳性能优于钴铬合金。

Objective: To compare the fatigue life of polyetheretherketone and cobalt chromium alloy snap rings at different concave depths, and provide a basis for the selection of clinical snap ring materials. The casting clasp made of polyetheretherketone and cobalt chromium alloy was correspondingly inserted into the two concave depths of the abutment teeth (0.25 mm and 0.50 mm), conduct displacement controlled fatigue bending experiments to obtain the initial load and number of cycles. The statistical analysis of the cyclic fatigue test results of the two materials’ snap rings showed that when the displacement was 0.25 mm, the initial load of cobalt chromium alloy was higher than that of polyetheretherketone (P 0.05). Conclusion: The fatigue resistance of polyetheretherketone is superior to that of cobalt chromium alloy.