通过宏观形貌观察、扫描电镜能谱以及现场轧辊分析,对201不锈钢冷轧钢带狭缝线质量缺陷的原因进行了分析研究。钢带在轧制过程中发生了平移,工作辊表面的锯齿状压痕往复运动是造成不锈钢带狭缝线产生的主要原因。
By means of macro morphology observation,scanning electron microscopy(SEM),energy dispersive spectroscopy(EDS)and on-site roll analysis,the causes of quality defects in the slit line of 201 stainless steel cold-rolled strip were analyzed and studied.The strip translation occurs during rolling,and the movement of zigzag indentation on the surface of work roll is the main reason for the slit line of stainless steel strip.
出处
《材料科学》
CAS
2019年第5期525-529,共5页
Material Sciences