Experimental Study on the Ultimate Shear Performance of Elastomeric Bearings of Doublefold Elastomeric Layer

Experimental Study on the Ultimate Shear Performance of Elastomeric Bearings of Doublefold Elastomeric Layer
下载PDF
导出
摘要 The elastomeric bearings shall not fail nor degrade the durability of the bridge due to the loss of its properties during its service life. Since the elastomeric bearings can be used in the seismic design complementarily to seismic devices, even if it is not a seismic isolator, they particularly should secure high shear performance. For elastomeric bearings to behave monolithically, the internal rubber which is located between the steel plates should be single rubber layer. In this study, a series of elastomeric bearings were fabricated and ultimate shear performance was investigated. Some specimens are of single elastomeric layer, the other are of doublefold elastomeric layer. Shear fatigue tests and ultimate shear tests were carried out. Tests results show that the elastomeric bearings whose internal rubber layer is formed by agglomeration of several rubber pads is likely to experience significant loss of its shear performance or early failure. The elastomeric bearings shall not fail nor degrade the durability of the bridge due to the loss of its properties during its service life. Since the elastomeric bearings can be used in the seismic design complementarily to seismic devices, even if it is not a seismic isolator, they particularly should secure high shear performance. For elastomeric bearings to behave monolithically, the internal rubber which is located between the steel plates should be single rubber layer. In this study, a series of elastomeric bearings were fabricated and ultimate shear performance was investigated. Some specimens are of single elastomeric layer, the other are of doublefold elastomeric layer. Shear fatigue tests and ultimate shear tests were carried out. Tests results show that the elastomeric bearings whose internal rubber layer is formed by agglomeration of several rubber pads is likely to experience significant loss of its shear performance or early failure.
机构地区 不详
出处 《Engineering(科研)》 2013年第1期92-96,共5页 工程(英文)(1947-3931)
关键词 ELASTOMERIC Bearings SHEAR Performance SHEAR FATIGUE TEST ULTIMATE SHEAR TEST Elastomeric Bearings Shear Performance Shear Fatigue Test Ultimate Shear Test
  • 相关文献

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部