摘要
In order to investigate the chloride ion penetration resistance of coal gangue concrete under multi-factor comprehensive action, the non-steady-state accelerated chloride ion migration test was used to test the chloride diffusion law of coal gangue concrete specimens by crack width, curing temperature and water-cement ratio. Three groups of crack width (0 mm, 0.05 - 0.12 mm, 0.12 - 0.2 mm), three curing temperatures (high temperature 45, medium temperature 25, low temperature 10), three water cement ratios (0.3, 0.4, 0.5) were set in the experiment. The results show that when the curing temperature and water cement ratio are constant, the crack width less than 0.12 mm has little effect on the chloride content and chloride diffusion coefficient. When the crack width is larger than 0.12 mm, the chloride penetration depth increases with the crack width. The resistance to chloride ion penetration of gangue concrete is greatly influenced by the water cement ratio. The influ-ence degree of three factors on chloride ion migration coefficient of gangue concrete is as follows: water cement ratio > crack width > curing temperature.
In order to investigate the chloride ion penetration resistance of coal gangue concrete under multi-factor comprehensive action, the non-steady-state accelerated chloride ion migration test was used to test the chloride diffusion law of coal gangue concrete specimens by crack width, curing temperature and water-cement ratio. Three groups of crack width (0 mm, 0.05 - 0.12 mm, 0.12 - 0.2 mm), three curing temperatures (high temperature 45, medium temperature 25, low temperature 10), three water cement ratios (0.3, 0.4, 0.5) were set in the experiment. The results show that when the curing temperature and water cement ratio are constant, the crack width less than 0.12 mm has little effect on the chloride content and chloride diffusion coefficient. When the crack width is larger than 0.12 mm, the chloride penetration depth increases with the crack width. The resistance to chloride ion penetration of gangue concrete is greatly influenced by the water cement ratio. The influ-ence degree of three factors on chloride ion migration coefficient of gangue concrete is as follows: water cement ratio > crack width > curing temperature.