The effect of different types of surface preparation with SiC abrasive paper on the shear bond strength (SBS) of superficial bovine dentin obtained from the incisal, middle and cervical thirds were evaluated. Dentin substrates were obtained with twenty specimens for each locationgrit combination. Superficial dentin was exposed and prepared to 120-, 320-, or 600-grit SiC;the dentin surfaces were treated with Optibond Solo Plus (Kerr) and polymerized for 20 s. The specimens were placed in a jig, filled with resin composite Z100 (3M-ESPE), polymerized for 40 s according to manufacturer’s instructions, and stored for 24 h at 37℃ and 100% humidity. After 24 h, SBS was measured using a loading testing machine (Ul-tradent) and expressed in megapascals. A two-way ANOVA and Tukey test were used for data analysis. No statistically significant effect of the location (P = 0.254) or interaction grit-location (P = 0.629) were observed on SBS. Statistically significant effect of the grit on the SBS was detected (P < 0.001) with 320-grit being statistically different from 600-grit (P = 0.011) and 120-grit (P < 0.001). No significant differences were observed between 600-grit and 120-grit (P = 0.413). Regardless of the location, 320-grit consistently showed the lowest SBS indicating that different surface grit preparations have an effect on dentin SBS values.
The effect of different types of surface preparation with SiC abrasive paper on the shear bond strength (SBS) of superficial bovine dentin obtained from the incisal, middle and cervical thirds were evaluated. Dentin substrates were obtained with twenty specimens for each locationgrit combination. Superficial dentin was exposed and prepared to 120-, 320-, or 600-grit SiC;the dentin surfaces were treated with Optibond Solo Plus (Kerr) and polymerized for 20 s. The specimens were placed in a jig, filled with resin composite Z100 (3M-ESPE), polymerized for 40 s according to manufacturer’s instructions, and stored for 24 h at 37℃ and 100% humidity. After 24 h, SBS was measured using a loading testing machine (Ul-tradent) and expressed in megapascals. A two-way ANOVA and Tukey test were used for data analysis. No statistically significant effect of the location (P = 0.254) or interaction grit-location (P = 0.629) were observed on SBS. Statistically significant effect of the grit on the SBS was detected (P < 0.001) with 320-grit being statistically different from 600-grit (P = 0.011) and 120-grit (P < 0.001). No significant differences were observed between 600-grit and 120-grit (P = 0.413). Regardless of the location, 320-grit consistently showed the lowest SBS indicating that different surface grit preparations have an effect on dentin SBS values.