摘要
Transparent relaxor ferroelectric ceramics of the system lanthanum modified lead magnesium niobate have been investigated for a variety of electro-optic properties could make these materials alternatives to (Pb,La)(Zr,Ti)O3. However, a study that relates the properties in function stoichiometric formula, it has not been analyzed heretofore. Therefore, in this work the effect of A-site substitution of La+3 in the characterization microstructural, structural, optical and electro-optical on (1-x)[Pb(1-3/2y)Lay(Mg1/3Nb2/3)O3]-xPbTiO3 and (1-z)[(1-x)Pb(Mg1/3Nb2/3)O3+xPbTiO3]+zLa2O3 has been performed. It was observed that the properties according to the stoichiometric formula and the PT had a maximum whose behavior was related to the addition of lanthanum in each stoichiometries.
Transparent relaxor ferroelectric ceramics of the system lanthanum modified lead magnesium niobate have been investigated for a variety of electro-optic properties could make these materials alternatives to (Pb,La)(Zr,Ti)O3. However, a study that relates the properties in function stoichiometric formula, it has not been analyzed heretofore. Therefore, in this work the effect of A-site substitution of La+3 in the characterization microstructural, structural, optical and electro-optical on (1-x)[Pb(1-3/2y)Lay(Mg1/3Nb2/3)O3]-xPbTiO3 and (1-z)[(1-x)Pb(Mg1/3Nb2/3)O3+xPbTiO3]+zLa2O3 has been performed. It was observed that the properties according to the stoichiometric formula and the PT had a maximum whose behavior was related to the addition of lanthanum in each stoichiometries.
基金
CAPES,FAPESP and CNPq for the financial support.