Chemical bath deposition technique has been used to deposit Ni-doped Sb2S3 thin films onto glass substrate. Doping was carried out by adding 1, 3 and 5 wt% of Ni. Bath temperature was kept as 10℃ and films were annealed at 250℃ under vacuum. Polycrystalline nature of films with an orthorhombic phase was analyzed by X-ray diffraction technique. Scanning electron microscopy was used for morphological study which shows that grains are spherical. Optical measurements using transmittance data indicated that films have a direct band gap of 1.00 - 2.60 eV with an absorption coefficient of ~104 cm<sup>-1</sup> in visible range. The average value of electrical conductivity was calculated as 1.66, 1.11 and 1.06 (Ω·cm)<sup>-1</sup> for as-deposited films and 1.90, 2.08 and 1.15 (Ω·cm)<sup>-1</sup> for annealed films while refractive indices were found as 2.18 - 3.38 and 1.91 - 3.74 respectively. The obtained films can be used for solar cell applications due to their good absorbing properties like higher absorption coefficient and refractive index values.
Chemical bath deposition technique has been used to deposit Ni-doped Sb2S3 thin films onto glass substrate. Doping was carried out by adding 1, 3 and 5 wt% of Ni. Bath temperature was kept as 10℃ and films were annealed at 250℃ under vacuum. Polycrystalline nature of films with an orthorhombic phase was analyzed by X-ray diffraction technique. Scanning electron microscopy was used for morphological study which shows that grains are spherical. Optical measurements using transmittance data indicated that films have a direct band gap of 1.00 - 2.60 eV with an absorption coefficient of ~104 cm<sup>-1</sup> in visible range. The average value of electrical conductivity was calculated as 1.66, 1.11 and 1.06 (Ω·cm)<sup>-1</sup> for as-deposited films and 1.90, 2.08 and 1.15 (Ω·cm)<sup>-1</sup> for annealed films while refractive indices were found as 2.18 - 3.38 and 1.91 - 3.74 respectively. The obtained films can be used for solar cell applications due to their good absorbing properties like higher absorption coefficient and refractive index values.
作者
Saima Mushtaq
Bushra Ismail
Muhammad Raheel
Aurang Zeb
Saima Mushtaq;Bushra Ismail;Muhammad Raheel;Aurang Zeb(Department of Applied Physics, Federal Urdu University of Arts, Science and Technology, Islamabad, Pakistan;Department of Chemistry, COMSATS Institute of Information Technology, Abbottabad, Pakistan;Department of General Studies, Jubail University College, Jubail Industrial City, KSA)