摘要
The amino poly-siloxane was modified with self-made polyether silicones by the crafts of emulsion polymerization. We studied the emulsifier, the dosage of emulsifier initiator, polyether/silane coupling agent, pH value. There are some results of the research indicated in the following. First, there are many factors for the hydrophilic amino-silicone softener both on the polymerization process and the performance, such as the proportion and amount of emulsifier, initiator dosage, the mass ratio of the polyether and hydrogen silicone oil, the choice of silicone coupling agent, and the ratio and dosage of polyether silicones silane coupling agent. Second, the amount of hydrogen of the hydrogen silicones and the choice of catalyst are the key points on the synthesis of polyether silicones. The amount of hydrogen should be low and the catalyst must be economical and efficient and its introduction should be small and times, other more the holding time is not too long. The next one is that, in the process of hydrolysis of silane coupling agent, we need some acid to adjust pH value, or they will be broken down. The most important one but not the last is that the epoxy group can improve the products low-temperature supple and the persistence of the finishing fabric, furthermore it can reduce yellowing and has a good stability of the inorganic salt, however, it will be destroyed if the reaction temperature for epoxy is too high. What’s more, it is very economical and environmental that the process of emulsion is simple and with less emulsifier.
The amino poly-siloxane was modified with self-made polyether silicones by the crafts of emulsion polymerization. We studied the emulsifier, the dosage of emulsifier initiator, polyether/silane coupling agent, pH value. There are some results of the research indicated in the following. First, there are many factors for the hydrophilic amino-silicone softener both on the polymerization process and the performance, such as the proportion and amount of emulsifier, initiator dosage, the mass ratio of the polyether and hydrogen silicone oil, the choice of silicone coupling agent, and the ratio and dosage of polyether silicones silane coupling agent. Second, the amount of hydrogen of the hydrogen silicones and the choice of catalyst are the key points on the synthesis of polyether silicones. The amount of hydrogen should be low and the catalyst must be economical and efficient and its introduction should be small and times, other more the holding time is not too long. The next one is that, in the process of hydrolysis of silane coupling agent, we need some acid to adjust pH value, or they will be broken down. The most important one but not the last is that the epoxy group can improve the products low-temperature supple and the persistence of the finishing fabric, furthermore it can reduce yellowing and has a good stability of the inorganic salt, however, it will be destroyed if the reaction temperature for epoxy is too high. What’s more, it is very economical and environmental that the process of emulsion is simple and with less emulsifier.