摘要
Single crystals of the tetraethylammonium dihydrogenmonophosphate bis trihydrogenmonophosphate [CH3CH2]4N+(H2PO4)(H3PO4)2(TEP), were grown by slow evaporation solution technique at room temperature. The compound was characterised by IR, Raman, differential thermal analysis (TG-DTA) and single crystal X-ray diffraction. It crystallizes in the monoclinic system (space group P21/c) with the following unit cell dimensions: a = 7.765 (2) , b = 16.531 (4) , c = 14.843 (2) , β = 100.99 (2)o, Z=4 , DX =1.67Mg.m-3, Dm=1.532Mg-3, λ (MoKa) = 0.71073 , u=0.384 mm-1, F(000)=991, T = 20 (2)o. The structure was solved by the direct method and refined to final R value of 0.0342 and Rw=0.107 for 3239 independent [(CH3CH2)4N]+ reflections. The structure consists of infinite parallel two-dimensional planes built of mutually , H3PO4 tetrahedra ?and cations connected by strong and hydrogen bonding. There are no contacts other than van der Waals interactions between the layers.
Single crystals of the tetraethylammonium dihydrogenmonophosphate bis trihydrogenmonophosphate [CH3CH2]4N+(H2PO4)(H3PO4)2(TEP), were grown by slow evaporation solution technique at room temperature. The compound was characterised by IR, Raman, differential thermal analysis (TG-DTA) and single crystal X-ray diffraction. It crystallizes in the monoclinic system (space group P21/c) with the following unit cell dimensions: a = 7.765 (2) , b = 16.531 (4) , c = 14.843 (2) , β = 100.99 (2)o, Z=4 , DX =1.67Mg.m-3, Dm=1.532Mg-3, λ (MoKa) = 0.71073 , u=0.384 mm-1, F(000)=991, T = 20 (2)o. The structure was solved by the direct method and refined to final R value of 0.0342 and Rw=0.107 for 3239 independent [(CH3CH2)4N]+ reflections. The structure consists of infinite parallel two-dimensional planes built of mutually , H3PO4 tetrahedra ?and cations connected by strong and hydrogen bonding. There are no contacts other than van der Waals interactions between the layers.