摘要
Contact angle of ethylene glycol and formamide on (100) faces of NaCl, KCl, and KBr single crystal was measured, and the specific surface free energy (SSFE) was calculated. Dispersion component of the SSFE was 90.57, 93.78, and 99.52 mN·m-1 for NaCl, KCl, and KBr, respectively. Polar component of the SSFE was 1.05, 0.65, and 0.45 mN·m-1 for NaCl, KCl, and KBr. Such a large ratio of dispersion component of SSFE results from the neutrality of the crystal surface of alkali halide. Lattice component of alkali halide is 780, 717 and 689 kJ·mol-1 for NaCl, KCl, and KBr. The larger lattice enthalpy decreases dispersion component, and increases polar component of the SSFE. The larger lattice enthalpy is considered to enhance the rumpling of the crystal surface more strongly, and such rumpling is considered to decrease the neutrality of the crystal surface.
Contact angle of ethylene glycol and formamide on (100) faces of NaCl, KCl, and KBr single crystal was measured, and the specific surface free energy (SSFE) was calculated. Dispersion component of the SSFE was 90.57, 93.78, and 99.52 mN·m-1 for NaCl, KCl, and KBr, respectively. Polar component of the SSFE was 1.05, 0.65, and 0.45 mN·m-1 for NaCl, KCl, and KBr. Such a large ratio of dispersion component of SSFE results from the neutrality of the crystal surface of alkali halide. Lattice component of alkali halide is 780, 717 and 689 kJ·mol-1 for NaCl, KCl, and KBr. The larger lattice enthalpy decreases dispersion component, and increases polar component of the SSFE. The larger lattice enthalpy is considered to enhance the rumpling of the crystal surface more strongly, and such rumpling is considered to decrease the neutrality of the crystal surface.