Evaluation of Cathodic Arc Deposited Thick CrAlSiN Coatings by Erosion Test

Evaluation of Cathodic Arc Deposited Thick CrAlSiN Coatings by Erosion Test
下载PDF
导出
摘要 CrAlSiN with thickness up to 16 μm was deposited on tungsten carbide via multi-deposition process by cathode arc deposition technique. Scratch and water-sand jet impingement erosion tests were carried out to evaluate the adhesion by determining the worn surface of the coatings. Results showed that the failure mode of the adhesion can be concluded that the weak bond of each CrAlSiN layer as compared to the strong bond between the coating and substrate. The average surface roughness of the coatings before the erosion test was about the same level. After the erosion test of 30 minutes, the eroded CrAlSiN coatings exhibited improved average surface roughness as compared to the original CrAlSiN coatings. Further increasing the erosion up to 60 minutes, the wear and minor peeling of the CrAlSiN coating between each layer was observed. A further research to improve the bond strength between each layer was needed. CrAlSiN with thickness up to 16 μm was deposited on tungsten carbide via multi-deposition process by cathode arc deposition technique. Scratch and water-sand jet impingement erosion tests were carried out to evaluate the adhesion by determining the worn surface of the coatings. Results showed that the failure mode of the adhesion can be concluded that the weak bond of each CrAlSiN layer as compared to the strong bond between the coating and substrate. The average surface roughness of the coatings before the erosion test was about the same level. After the erosion test of 30 minutes, the eroded CrAlSiN coatings exhibited improved average surface roughness as compared to the original CrAlSiN coatings. Further increasing the erosion up to 60 minutes, the wear and minor peeling of the CrAlSiN coating between each layer was observed. A further research to improve the bond strength between each layer was needed.
出处 《Journal of Materials Science and Chemical Engineering》 2015年第1期66-71,共6页 材料科学与化学工程(英文)
关键词 Cathodic ARC EVAPORATION CrAlSiN COATING EROSION Cathodic Arc Evaporation CrAlSiN Coating Erosion
  • 相关文献

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部