Polycrystalline samples of Lead free (K0.5Na0.5)1-x(Li)x(Sb)x(Nb)1-xO3 ceramics with nominal compositions (x = 0.040 to 0.060) have been prepared by high temperature solid state reaction technique. X-ray diffraction (XRD) pattern shows that the crystal structure transforms from orthorhombic to tetragonal as Li and Sb content increases. Normal sintering process yield compounds with density ~98.2% of the theoretical value. Densification of the Li and Sb co-doped KNN ceramics might be explained by the liquid-phase sintering. This may be attributed to the low melting temperature of Li compounds that appears to promote the formation of a liquid phase during sintering.
Polycrystalline samples of Lead free (K0.5Na0.5)1-x(Li)x(Sb)x(Nb)1-xO3 ceramics with nominal compositions (x = 0.040 to 0.060) have been prepared by high temperature solid state reaction technique. X-ray diffraction (XRD) pattern shows that the crystal structure transforms from orthorhombic to tetragonal as Li and Sb content increases. Normal sintering process yield compounds with density ~98.2% of the theoretical value. Densification of the Li and Sb co-doped KNN ceramics might be explained by the liquid-phase sintering. This may be attributed to the low melting temperature of Li compounds that appears to promote the formation of a liquid phase during sintering.