摘要
The work presents the possibility of substitution of expensive, wear resistant Co-WC powders, that have been traditionally used in the production of sintered diamond tools, with cheap iron-base counterparts manufactured by ball milling. It has been shown that ball-milled Fe-Ni-Cu-Sn-C powders can be consolidated to a virtually pore-free condition by hot pressing at 900 ℃. The as-consolidated material has nanocrystalline structure and is characterised by a combination of high hardness, mechanical strength and excellent resistance to abrasion. Its properties can be widely modified by changing the milling conditions.
The work presents the possibility of substitution of expensive, wear resistant Co-WC powders, that have been traditionally used in the production of sintered diamond tools, with cheap iron-base counterparts manufactured by ball milling. It has been shown that ball-milled Fe-Ni-Cu-Sn-C powders can be consolidated to a virtually pore-free condition by hot pressing at 900 ℃. The as-consolidated material has nanocrystalline structure and is characterised by a combination of high hardness, mechanical strength and excellent resistance to abrasion. Its properties can be widely modified by changing the milling conditions.