Improvement of Sliding Performance for Ball on Disc Tribo-Partners Using Graphite Like Carbon Solid Lubricant Coating 被引量:1

Improvement of Sliding Performance for Ball on Disc Tribo-Partners Using Graphite Like Carbon Solid Lubricant Coating
下载PDF
导出
摘要 Sliding wear tests of chilled cast iron tappet-disc and cam-ball tribo-partners were conducted by using ball on disc testing device. Magnetron sputtering CrTiAlN hard coating and Graphite like carbon (GLC) solid lubricant coatings were applied on either one or both of the contact surfaces on tribo-partners. Ball crater device and scanning electron microscope were used to investigate surface wear of rubbed track on disc and wear scar on ball. The sliding performances of tribo-partners were evaluated in terms of coefficient of friction at sliding surfaces and specific wear rate (SWR) on both of the rubbed surfaces under specific test conditions. All test results showed that GLC solid lubricant coating on both surfaces of tappet-disc and cam-ball was the best option to allow this tribo-partners having high performance in terms of sliding under high load with low coefficient of friction and low SWR. The advantage of using GLC solid lubricant coating is to enable mechanical parts made of ordinary and sustainable materials (e.g. cast iron or plain steels) to be operated under even harsher conditions of higher load and higher wear environment with improved performance. Sliding wear tests of chilled cast iron tappet-disc and cam-ball tribo-partners were conducted by using ball on disc testing device. Magnetron sputtering CrTiAlN hard coating and Graphite like carbon (GLC) solid lubricant coatings were applied on either one or both of the contact surfaces on tribo-partners. Ball crater device and scanning electron microscope were used to investigate surface wear of rubbed track on disc and wear scar on ball. The sliding performances of tribo-partners were evaluated in terms of coefficient of friction at sliding surfaces and specific wear rate (SWR) on both of the rubbed surfaces under specific test conditions. All test results showed that GLC solid lubricant coating on both surfaces of tappet-disc and cam-ball was the best option to allow this tribo-partners having high performance in terms of sliding under high load with low coefficient of friction and low SWR. The advantage of using GLC solid lubricant coating is to enable mechanical parts made of ordinary and sustainable materials (e.g. cast iron or plain steels) to be operated under even harsher conditions of higher load and higher wear environment with improved performance.
出处 《Materials Sciences and Applications》 2018年第1期191-209,共19页 材料科学与应用期刊(英文)
关键词 SLIDING Wear Tribo-Partners GRAPHITE LUBRICANT Coating Sliding Wear Tribo-Partners Graphite Lubricant Coating
  • 相关文献

同被引文献6

引证文献1

二级引证文献2

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部