摘要
Surface texture of the mouthguard affects the sense of adaptation in the athlete and further affects hygiene. Therefore, finish polishing is extremely important. The aim of this study was to investigate the difference in the surface roughness after finishing polishing of ethylene-vinyl-acetate (EVA) sheets and after application of the finishing liquid, and to evaluate its effectiveness. Total of 48 specimens of EVA (3 × 3 mm) were divided into 4 groups according to polishing condition (control = unpolished;condition A = Robinson-brush;condition B = Lisko-Fine, and condition C = Mouthguard-wheel). Polishing was performed at low speed by using a straight headpiece. The rotation speeds were 5000, 4000 and 6000 rpm for condition A, B, and C, respectively. Next, a finishing liquid was applied to each specimen. For application, a cotton swab was used, and it was applied by three reciprocations. A non-contact surface shape measuring machine was used for measuring surface roughness;the measurement range is 1.65 mm and the resolution is 0.01 nm. The arithmetic average height (Sa) was measured. The differences in the surface roughness before and 15 min after the application of the finishing liquid were analyzed by two-way analysis of variance and Bonferroni’s multiple comparison tests. Surface roughness of the specimen before application became coarse in the order of control, condition C, B and A, and Sa was about 0.20, 1.98, 2.92, and 4.71 μm, respectively. The degree of reduction in roughness was about 1.0 μm or more than each polished state in conditions A and B. Condition C was not significantly different before and after application. No significant difference was observed between condition B and C after application. The results of this study showed that the surface roughness decreased due to the application of the finishing liquid when the surface roughness after finish polishing was about 2.0 μm or more.
Surface texture of the mouthguard affects the sense of adaptation in the athlete and further affects hygiene. Therefore, finish polishing is extremely important. The aim of this study was to investigate the difference in the surface roughness after finishing polishing of ethylene-vinyl-acetate (EVA) sheets and after application of the finishing liquid, and to evaluate its effectiveness. Total of 48 specimens of EVA (3 × 3 mm) were divided into 4 groups according to polishing condition (control = unpolished;condition A = Robinson-brush;condition B = Lisko-Fine, and condition C = Mouthguard-wheel). Polishing was performed at low speed by using a straight headpiece. The rotation speeds were 5000, 4000 and 6000 rpm for condition A, B, and C, respectively. Next, a finishing liquid was applied to each specimen. For application, a cotton swab was used, and it was applied by three reciprocations. A non-contact surface shape measuring machine was used for measuring surface roughness;the measurement range is 1.65 mm and the resolution is 0.01 nm. The arithmetic average height (Sa) was measured. The differences in the surface roughness before and 15 min after the application of the finishing liquid were analyzed by two-way analysis of variance and Bonferroni’s multiple comparison tests. Surface roughness of the specimen before application became coarse in the order of control, condition C, B and A, and Sa was about 0.20, 1.98, 2.92, and 4.71 μm, respectively. The degree of reduction in roughness was about 1.0 μm or more than each polished state in conditions A and B. Condition C was not significantly different before and after application. No significant difference was observed between condition B and C after application. The results of this study showed that the surface roughness decreased due to the application of the finishing liquid when the surface roughness after finish polishing was about 2.0 μm or more.
