摘要
The sawdust reinforced Acrylonitrile Butadiene Styrene (ABS) composites were prepared by using hot press molding machine for five different wt% (0%, 5%, 10%, 15% and 20%) at 180<span style="white-space:nowrap;">°</span>C temperature and 50 KN load. Sawdust was collected from local saw mill of Savar, Dhaka, Bangladesh and ABS polymer was collected from local market of Dhaka, Bangladesh. In this study, different properties of composites like physical (bulk density and water absorption), mechanical (tensile properties and hardness) and structural (Fourier Transform Infrared Spectroscopy) properties were studied. The bulk density of composites was not altered consistently and it gave greater value for 5% and 20% composites. The water absorption enhanced for all composites with the accumulation of fiber content and soaking time. The reduction of tensile strength and Leeb’s rebound hardness of the composites were observed with the increase of the fiber content in all compositions. Maximum (%) of elongation was found for 5% composite, and then it gradually decreased;however, elastic modulus increased with the increased of fiber content in composites. Fourier Transform Infrared (FTIR) spectroscopy study was done for structural characterization. It was found that there was a new bond (C≡C) stretching formed for 20% composite;moreover, C-H rocking for 0% composite was broken for all other composites after the addition of sawdust in ABS polymer matrix.
The sawdust reinforced Acrylonitrile Butadiene Styrene (ABS) composites were prepared by using hot press molding machine for five different wt% (0%, 5%, 10%, 15% and 20%) at 180<span style="white-space:nowrap;">°</span>C temperature and 50 KN load. Sawdust was collected from local saw mill of Savar, Dhaka, Bangladesh and ABS polymer was collected from local market of Dhaka, Bangladesh. In this study, different properties of composites like physical (bulk density and water absorption), mechanical (tensile properties and hardness) and structural (Fourier Transform Infrared Spectroscopy) properties were studied. The bulk density of composites was not altered consistently and it gave greater value for 5% and 20% composites. The water absorption enhanced for all composites with the accumulation of fiber content and soaking time. The reduction of tensile strength and Leeb’s rebound hardness of the composites were observed with the increase of the fiber content in all compositions. Maximum (%) of elongation was found for 5% composite, and then it gradually decreased;however, elastic modulus increased with the increased of fiber content in composites. Fourier Transform Infrared (FTIR) spectroscopy study was done for structural characterization. It was found that there was a new bond (C≡C) stretching formed for 20% composite;moreover, C-H rocking for 0% composite was broken for all other composites after the addition of sawdust in ABS polymer matrix.
作者
Budrun Neher
Nabila Tasnim Nova
Rakib Hossain
M. A. Gafur
Farid Ahmed
Budrun Neher;Nabila Tasnim Nova;Rakib Hossain;M. A. Gafur;Farid Ahmed(Department of Physics, Jahangirnagar University, Dhaka, Bangladesh;Department of Physics, Bangabandhu Sheikh Mujibur Rahman Science & Technology University, Gopalganj, Bangladesh;PP and PDC, Bangladesh Council of Scientific and Industrial Research, Dhaka, Bangladesh)