The DC conductivity and dielectric properties of glassy Se100–xZnx 2 ≤ x ≤ 20 alloys have been investigated in the temperature range 303 - 487 K with frequency range 100 Hz – 1 MHz. It is observed that DC conductivity decreases and the activation energy increases with Zn content in Se-Zn system. Dielectric dispersion is observed when Zn incorporated in Se-Zn glassy system. The results are explained on the basis of DC conduction mechanism and dipolar-type dielectric dispersion.
The DC conductivity and dielectric properties of glassy Se100–xZnx 2 ≤ x ≤ 20 alloys have been investigated in the temperature range 303 - 487 K with frequency range 100 Hz – 1 MHz. It is observed that DC conductivity decreases and the activation energy increases with Zn content in Se-Zn system. Dielectric dispersion is observed when Zn incorporated in Se-Zn glassy system. The results are explained on the basis of DC conduction mechanism and dipolar-type dielectric dispersion.