摘要
Between all precursors of copper complex, bis-(acetylacetonato)-copper (II) and bis-oxalate copper (II) with very close structures are two of the best representatives for copper nanoparticles synthesis. In this research, only bis-(acetylacetonato)-copper (II) in presence of some effective non-ionic surfactants such as Triton X-100, Dodecylamine, Tween 80 and also triphenylphosphine as a reducing agent via thermal decomposition process was used for copper nanopaticles synthesis. Two shif-base E19 and E22 complexes were also used for the investigation of these kinds of shif-base complexes capabilities by this method as precursors and all results were compared with each other. Between all surfactants, Triton X-100 gave the best yield with the largest grains. The techniques used for characterization of copper nanoparticles were TEM, EDX, FT-IR and XRD. TG-DTA and CV were used for characterization of bis-(acetylacetonato)-copper (II) complex.
Between all precursors of copper complex, bis-(acetylacetonato)-copper (II) and bis-oxalate copper (II) with very close structures are two of the best representatives for copper nanoparticles synthesis. In this research, only bis-(acetylacetonato)-copper (II) in presence of some effective non-ionic surfactants such as Triton X-100, Dodecylamine, Tween 80 and also triphenylphosphine as a reducing agent via thermal decomposition process was used for copper nanopaticles synthesis. Two shif-base E19 and E22 complexes were also used for the investigation of these kinds of shif-base complexes capabilities by this method as precursors and all results were compared with each other. Between all surfactants, Triton X-100 gave the best yield with the largest grains. The techniques used for characterization of copper nanoparticles were TEM, EDX, FT-IR and XRD. TG-DTA and CV were used for characterization of bis-(acetylacetonato)-copper (II) complex.