Polyurethane-imide elastomers (PUIEs) are formed from isocyanate, polyol, acid anhydride, and diamine by liquid polymerization. Unfortunately, many of the diamines have rarely been applied to the formation of PUIEs. Hence, investigating the effect of diamines on PUIEs remains a challenge in polymer chemistry. Herein, PUIEs prepared from 4,4'-diphenylmethane diisocyanate (MDI), polytetramethylene glycol (Mw: 1000), pyromellitic dianhydride, and aromatic diamines (such as p-phenylene diamine, 4,4'-oxydianiline, and 1,3-bis(4-aminophenoxy)benzene), and aliphatic diamines (such as 1,2-ethylene diamine, 1,6-hexamethylene diamine, and 1,12-dodecamethylene diamine) were synthesized by liquid polymerization. The morphologies and the chemical, thermal, and mechanical properties of the various PUIEs were investigated. The obtained elastomeric sheets were characterized in terms of the following tests and methods: solubility and swelling tests, X-ray diffraction and differential scanning calorimetry, dynamic mechanical analysis and thermogravimetric analysis, tensile tests, nuclear magnetic resonance spectroscopy, infrared spectroscopy, atomic force microscopy, contact angle microscopy, and scanning electron
Polyurethane-imide elastomers (PUIEs) are formed from isocyanate, polyol, acid anhydride, and diamine by liquid polymerization. Unfortunately, many of the diamines have rarely been applied to the formation of PUIEs. Hence, investigating the effect of diamines on PUIEs remains a challenge in polymer chemistry. Herein, PUIEs prepared from 4,4'-diphenylmethane diisocyanate (MDI), polytetramethylene glycol (Mw: 1000), pyromellitic dianhydride, and aromatic diamines (such as p-phenylene diamine, 4,4'-oxydianiline, and 1,3-bis(4-aminophenoxy)benzene), and aliphatic diamines (such as 1,2-ethylene diamine, 1,6-hexamethylene diamine, and 1,12-dodecamethylene diamine) were synthesized by liquid polymerization. The morphologies and the chemical, thermal, and mechanical properties of the various PUIEs were investigated. The obtained elastomeric sheets were characterized in terms of the following tests and methods: solubility and swelling tests, X-ray diffraction and differential scanning calorimetry, dynamic mechanical analysis and thermogravimetric analysis, tensile tests, nuclear magnetic resonance spectroscopy, infrared spectroscopy, atomic force microscopy, contact angle microscopy, and scanning electron microscopy