Corrosion inhibition of mild steel in 0.5 mol/L H<sub>2</sub>SO<sub>4</sub> was investigated in the absence and presence of different concentrations of thiosemicarbazide. The inhibition efficiency of thiosemicarbazide was studied by electrochemical impedance methods, potentiodynamic polarization and scanning electron microscopy at different inhibitor concentrations. Inhibition efficiency, corrosion rate and surface coverage were evaluated at different concentrations of thiosemicarbazide. Electrochemical impedance plots indicated that the presence of the inhibitors increased the charge transfer resistance of the corrosion process, increasing the inhibition efficiency. Polarization curves showed that this compound acted as mixed type inhibitor. The results of the investigation showed that this compound had good inhibiting properties for mild steel corrosion in 0.5 M sulfuric acid. The adsorption isotherm studies showed that Thiosemicarbazide adsorbed chemisorbed and formed a stable surface complex on the mild steel surface. And Langmuir obeyed the adsorption isotherm. Scanning electron microscopy analysis shows that, the surface morphology of the polished mild steel in the presence of thiosemicarbazide as inhibitor is smoother surface as compared with polished mild steel specimen in the absence of inhibitor.
Corrosion inhibition of mild steel in 0.5 mol/L H<sub>2</sub>SO<sub>4</sub> was investigated in the absence and presence of different concentrations of thiosemicarbazide. The inhibition efficiency of thiosemicarbazide was studied by electrochemical impedance methods, potentiodynamic polarization and scanning electron microscopy at different inhibitor concentrations. Inhibition efficiency, corrosion rate and surface coverage were evaluated at different concentrations of thiosemicarbazide. Electrochemical impedance plots indicated that the presence of the inhibitors increased the charge transfer resistance of the corrosion process, increasing the inhibition efficiency. Polarization curves showed that this compound acted as mixed type inhibitor. The results of the investigation showed that this compound had good inhibiting properties for mild steel corrosion in 0.5 M sulfuric acid. The adsorption isotherm studies showed that Thiosemicarbazide adsorbed chemisorbed and formed a stable surface complex on the mild steel surface. And Langmuir obeyed the adsorption isotherm. Scanning electron microscopy analysis shows that, the surface morphology of the polished mild steel in the presence of thiosemicarbazide as inhibitor is smoother surface as compared with polished mild steel specimen in the absence of inhibitor.
作者
Fatma Mohamed Mahgoub
S. M. Al-Rashdi
Fatma Mohamed Mahgoub;S. M. Al-Rashdi(Chemistry Department, Faculty of Science, King Abdulaziz University, Jeddah, KSA;Institute of Graduate Studies and Research, University of Alexandria, Alexandria, Egypt;Chemistry Department, Faculty of Science, Umm Al-Qura University, Makka, KSA)