摘要
In this study, a novel flocculant was prepared by an inorganic polymetric flocculant (IPF) - polysilicate ferro- aluminum sulfate (PSFA) and rectorite (REC). The structure of the PSFA-REC composite was characterized by Fourier transform infrared (FT-IR) spectroscopy and X-ray diffraction (XRD), in order to determine the optimal temperature. The flocculation test was made at 25℃, 45℃ and 65℃, the results indicated that when the temperature was 65℃, the removal efficiency of the oil and COD was the best, which was 87.2% and 92.6% respectively. Then by comparisons among rectorite (REC), PSFA and the composite PSFA-REC at the temperature of 65℃ and the optimal dosage of 11 mg/L, the composite PSFA-REC showed better flocculation performance than flocculant REC and PSFA alone.
In this study, a novel flocculant was prepared by an inorganic polymetric flocculant (IPF) - polysilicate ferro- aluminum sulfate (PSFA) and rectorite (REC). The structure of the PSFA-REC composite was characterized by Fourier transform infrared (FT-IR) spectroscopy and X-ray diffraction (XRD), in order to determine the optimal temperature. The flocculation test was made at 25℃, 45℃ and 65℃, the results indicated that when the temperature was 65℃, the removal efficiency of the oil and COD was the best, which was 87.2% and 92.6% respectively. Then by comparisons among rectorite (REC), PSFA and the composite PSFA-REC at the temperature of 65℃ and the optimal dosage of 11 mg/L, the composite PSFA-REC showed better flocculation performance than flocculant REC and PSFA alone.